Influence of the thickness of the coating of the elements of reinforced concrete exposed to corrosion processes and subjected to external loads

  • R. S. Meneses Departamento de Ingeniería, Universidad Nacional del Sur, Bahía Blanca, Argentina.
  • J. M. Moro Departamento de Ingeniería, Universidad Nacional del Sur, Bahía Blanca, Argentina.
  • R. R. Aveldaño Departamento de Ingeniería, Universidad Nacional del Sur, Bahía Blanca, Argentina.
  • N. F. Ortega Departamento de Ingeniería, Universidad Nacional del Sur, Bahía Blanca, Argentina.

Abstract


Influence of the thickness of the coating of the elements of reinforced concrete exposed to corrosion processes and subjected to external loads

ABSTRACT

When studies are done in reinforced concrete, it is important to consider the action of external loads, since that is the most common situation in structures. In this study we present the results of exposing reinforced concrete beams to a process of accelerated corrosion, while under bending stresses caused by loads that generate equal tensile stresses on the corroded reinforcements. The beams were built with different cover thicknesses over the reinforcements, and with a 25 MPa characteristic resistance concrete. This study shows the influence of the cover thickness over the corrosion process and its external manifestation (cover cracking), under the same mechanical stress.

Keywords: tension corrosion reinforcement; cover; cracking.


Influência da espessura de cobrimento dos elementos de concreto armado expostos a processos de corrosão e submetidos a cargas externas

RESUMO

Ao realizar estudos sobre corrosão em concreto armado, é importante considerar nos ensaios a ação de cargas externas, pois esta situação é mais frequente nas estruturas. Neste artigo apresentam-se os resultados obtidos ao expor vigas de concreto armado a um processo de corrosão acelerada, submetidas a esforços de flexão materializados com cargas que geram tensões constantes de tração nas armaduras corroídas. As vigas foram elaboradas com diferentes espessuras de cobrimento das armaduras e com um concreto de resistência característica de 25MPa. Este estudo coloca em evidência a influência da espessura de cobrimento das armaduras, sobre o processo de corrosão e sua manifestação externa (fissuração do cobrimento), frente às mesmas solicitações mecânicas.

Palavras-chave: corrosão de armaduras tracionadas; cobrimento; fissuração.

 

Influencia del espesor del recubrimiento de elementos de hormigón armado expuestos a procesos de corrosión y sometidos a cargas externas

RESUMEN

Al realizar estudios sobre corrosión en hormigón armado, es importante considerar en los ensayos, la acción de cargas externas, pues esta situación es la más frecuente en las estructuras. En este trabajo, se presentan los resultados obtenidos al exponer a un proceso de corrosión acelerada, a vigas de hormigón armado sometidas a esfuerzos flexionales, materializados con cargas, que generan iguales tensiones de tracción en las armaduras corroídas. Las vigas se fabricaron con diferentes espesores de recubrimiento de las armaduras y con un hormigón de resistencia característica 25 MPa. Este estudio pone en evidencia la influencia del espesor de recubrimiento de las armaduras, sobre el proceso de corrosión y su manifestación externa (fisuración del recubrimiento), frente a las mismas solicitaciones mecánicas.

Palabras claves: corrosión de armaduras traccionadas; recubrimiento; fisuración.

Downloads

Download data is not yet available.

References

Almusallam, A. A., Al-Gahtani, A. S., Aziz, A. R. (1996), “Effect of reinforcement corrosion on bond strengthâ€, Construction and Building Materials, V. 10, No. 2, pp. 123-129.

Alonso, M. C., Andrade, C., Rodríguez, J., Diez, J. M. (1998), “Factors controlling cracking in concrete affected by reinforcement corrosionâ€, Materials and Structures, Nr. 31, pp. 435-445.

Alonso, M. C., Andrade, M. C., Rodríguez, J., Casal, J., García, M. (1994), “Evaluación experimental de la fisuración del hormigón producida por la corrosión de las armadurasâ€, Hormigón y Acero, No. 194, pp. 29-42.

Al-Sulaimani, J., Kaleemullah, M., Basunbul, I. A., Rasheeduzafar (1990), “Influence on corrosion and cracking on bond behaviour and strength of reinforced concrete membersâ€, ACI Structural Journal, V. 87, Nr 2, pp. 220-231.

American Society for Testing and Materials: ASTM C876, “Standard test method for half cell potential of reinforcing steel in concreteâ€, Philadelphia, U.S.A, (1980).

Andrade, M. C., Alonso, M. C., Molina, F. J. (1993), “Cover cracking as a function of bar corrosion: Part I – Experimental testâ€, Materials and Structures, Nr. 26, pp. 453-464.

Aveldaño, R. R., Ortega, N. F. (2009), “Influence of reinforcement distribution in the corrosive process of reinforced concrete beamsâ€, Magazine of Concrete Research, Thomas Telford, V. 61, Nr. 3, pp. 213-220.

Aveldaño, R. R., Ortega, N. F. (2011),“Characterization of Concrete Cracking due to Corrosion of Reinforcements in Different Environmentsâ€, Construction and Building Materials,V.25, pp.630-37.

Aveldaño, R. R., Ortega, N. F.(2013), “Behavior of concrete elements subjected to corrosion in their compressed or tensed reinforcementâ€, Construction and Building Materials, Nr. 38, pp. 822–828.

Calabrese, L., Campanella, G., Proverbio, E. (2013), “Identification of corrosion mechanisms by univariate and multivariate statistical analysis during long term acoustic emission monitoring on a pre-stressed concrete beamâ€, Corrosion Science, V. 73, pp. 161-171.

Elfergani, H. A., Rhys, P., Holford, K. M. (2013), “Damage assessment of corrosion in prestressed concrete by acoustic emissionâ€, Construction and Building Materials, V. 40, pp. 925–933.

Fumin, L., Yingshu, Y., Chun-Qing, L. (2011), “Corrosion propagation of prestressing steel strands in concrete subject to chloride attackâ€, Construction and Building Materials, V. 25, Nr. 10, pp. 3878-3885.

Hariche, L., Ballim, Y., Bouhicha, M. Kenai, S. (2012), “Effects of reinforcement configuration and sustained load on the behaviour of reinforced concrete beams affected by reinforcing steel corrosionâ€, Cement and Concrete Composites, V. 34, Nr. 10, pp. 1202–1209.

Instituto Argentino de Normalización y Certificación IRAM 1627: “Agregados. Granulometría de los agregados para hormigónâ€, Buenos Aires, (1997).

Instituto Argentino de Racionalización de Materiales – Instituto Argentino de Siderurgia, Norma U 500-528: “Barras de acero conformadas de dureza natural, para armadura en estructuras de hormigónâ€, Buenos Aires, (1989).

Instituto Argentino de Normalización y Certificación IRAM 1871: “Método de ensayo para determinar la capacidad y la velocidad de succión capilar de agua del hormigón endurecidoâ€, Buenos Aires, (2005).

Instituto Argentino de Normalización y Certificación IRAM 1546: “Hormigón de cemento portland. Método de ensayo de compresiónâ€, Buenos Aires, (1992).

Instituto Argentino de Normalización y Certificación IRAM 1658: Hormigón. “Método de ensayo de tracción simple por compresión diametralâ€, Buenos Aires, (1995).

Instituto Argentino de Normalización y Certificación IRAM 1534: “Hormigón de cemento portland. Preparación y curado de probetas para ensayos en laboratorioâ€, Buenos Aires, (1985).

Malumbela, G., Moyo, P., Alexander, M., (2009), “Behaviour of RC beams under sustained service loadsâ€, Construction and Building Materials, V. 23, Nr. 11, pp. 3346–3351.

Melchers, R. (2001), “Assessment of existing structures, approaches and research needsâ€, Journal of Structural Engineering, ASCE, pp. 406-411.

Moro, J.M., Meneses, R.S., Ortega, N.F., Aveldaño, R.R., Señas, L., Priano C.V., “Corrosión de Armaduras en Estructuras de Hormigón Reciclado con Tratamientos Previosâ€, CINPAR 2012, VIII Congreso Internacional sobre Patología y Recuperación de Estructuras, (2012), 11 páginas.

Ortega, N. F., Alonso, M. C., Andrade, M. C., López, C., “Análisis de la fisuración ocasionada por la corrosión de las armaduras activas de elementos pretensadosâ€, Coloquia, Madrid, (2001).

Peralta, M. H., Rivas, I. E., Ortega, N. F. (2006), “Análisis Numérico de la Fisuración Superficial de Estructuras de Hormigón Armado por Efecto de la Corrosiónâ€, Informes de la Construcción, V. 58, No. 501, pp. 51-58.

Rodríguez, J., Ortega, L. M., Casal, J., Vidal, M. A. (1993), “Disminución de la adherencia entre hormigón y barras corrugadas debido a la corrosiónâ€, Hormigón y Acero, No 189, pp. 49-65.

Rodríguez, J., Ortega, L. M., García, A. M. (1993), “Medida de la velocidad de corrosión de las armaduras en estructuras de hormigón, mediante un equipo desarrollado dentro del proyecto Eureka EU 401â€, Hormigón y Acero, No. 189, pp. 79-91.

Rodríguez, J., Ortega Basagoiti, L. M., Casal, J., Diez, J. M. (1996), “Comportamiento estructural de vigas de hormigón con armaduras corroídasâ€, Hormigón y Acero, No. 200, pp.113-131.

Rodríguez, J., Ortega Basagoiti, L. M., Casal, J., Diez, J. M. (1998), “La corrosión de armaduras y la vida residual de las estructuras de hormigónâ€, Hormigón y Acero, No. 208, pp. 63-78.

Schierloh M. I., “Corrosión de armaduras. Características que debe tener el hormigón para aumentar la protecciónâ€, Tesis de Magíster en Ingeniería, Departamento de Ingeniería, Universidad Nacional del Sur, Director de Tesis: Ortega N.F., (2003).

Schierloh M. I., Ortega N. F., Señas L. N.; “Relación entre Algunas Propiedades del Hormigón del

Recubrimiento y el Proceso Corrosivo de las Armadurasâ€, 14° Reunión de Asociación Argentina de Tecnología del Hormigón, (2001), pp. 125-132.

Torres-Acosta, A. A., Navarro-Gutierrez, S., Terán-Guillén, J. (2007), “Residual flexure capacity of corroded reinforced concrete beamsâ€, Engineering Structures, V. 29, Nr. 6, pp. 1145-1152.

Tuutti K. (1982); “Corrosion of steel in concreteâ€, Swedish Cement and Concrete Institute (CIB) pp. 4-82, Stockholm, Sweden

Yu, L., François, R., Dang, V. H., L'Hostis, V., Gagné, R., “Development of chloride-induced corrosion in pre-cracked RC beams under sustained loading: Effect of load-induced cracks, concrete cover, and exposure conditionsâ€, Cement & Concrete Research, Nº67, 2015, pp.246-258.

Published
2016-05-31
How to Cite
Meneses, R. S., Moro, J. M., AveldañoR. R., & Ortega, N. F. (2016). Influence of the thickness of the coating of the elements of reinforced concrete exposed to corrosion processes and subjected to external loads. Revista ALCONPAT, 6(2), 129 - 144. https://doi.org/10.21041/ra.v6i2.134
Section
Applied Research